PPS-SGC301LFRT

LFRT PPS

PPS-SGC301LFRT is a 30% long CF reinforced linear polyphenylene sulfide.

  • Property
  • Unit
  • Test Standard
  • Value
  • Physical properties
  •  
  •  
  •  
    • Density kg/m³ ISO 1183 1450
    Mold shrinkage(Machine Direction) % GB/T 15585
    Mold shrinkage(Transverse Direction) % GB/T 15585
    Water absorption (23°C-sat) % ISO 62

  • Mechanical properties
  •  
  •  
  •  
    • Tensile stress MPa ISO 527 200
    Elongation at Break (at Break) % ISO 527 0.7
    Flexural Modulus GPa ISO 178 30
    Flexural Strength MPa ISO178 340
    Charpy Impact Strength（V-notched） kJ/m² IS0 179 14

  • Thermal properties
  •  
  •  
  •  
    • Melting temperature (10°C/min) °C ISO 11357
    Heat Deflection Tem p High Load（1.8MPa） °C ISO 75 280
    Flammability class UL-94 V-0

  • Electrical properties
  •  
  •  
  •  
    • Dielectric Strength KV/mm IEC 60243
    Dielectric Constant
    		IEC 60250
    Dissipation Factor
    		IEC 60250
    Volume resistivity Ω•cm IEC 60093
    CTI V IEC 60112

  • Test specimen production
  •  
  •  
  •  
    • Drying

    		150℃&3h/120℃&5h
    Injection Pressure MPa

    Injection molding melt temperature °C ISO 294 285~345 
    Injection molding mold temperature °C ISO 294 140~160
    Limit in-cylinder retention time