RS-SG320REL is a kind of polyphenylene sulfide which is unreinforced,impact-modified and possess of high melt viscosity suitable for extrusion.
Density | kg/m³ | ISO 1183 | 1200 |
Mold shrinkage | % | GB/T 15585 | 2.0 |
Water absorption (23°C-sat) | % | ISO 62 | 0.1 |
Tensile stress | MPa | ISO 527 | 40 |
Elongation at Break (at Break) | % | ISO 527 | 80 |
Flexural Modulus | MPa | ISO 178 | 1500 |
Flexural Strength | MPa | ISO178 | 60 |
Charpy Impact Strength(V-notched) | kJ/m² | IS0 179 | 50 |
Heat Deflection Tem p High Load(1.8MPa) |
°C | ISO 75 | 90 |
Flammability | class | UL-94 | V-1 |
Dielectric Strength | KV/mm | IEC 60243 | 24 |
Dielectric Constant |
|
IEC 60250 | 3.0 |
Dissipation Factor |
|
IEC 60250 | 0.002 |
Drying |
|
|
80℃&5h |
Hopper temperature | °C |
|
20~40 |
Extruder Zone temperature | °C |
|
300~320 |
Adaptor temperature | °C |
|
290~310 |
Die temperature |
°C |
|
300~320 |