PPS-SGM605E43

Glass Fiber&Mineral Compounds PPS

PPS-SGM605E43 PPS is a 60% glass fiber and mineral reinforced polyphenylene sulfide compound developed to provide high modulus, low warp, good mechanical and electrical performance and low cost.

  • Property
  • Unit
  • Test Standard
  • Value
  • Physical properties
  •  
  •  
  •  
  • Density kg/m³ ISO 1183 1900
    Mold shrinkage(Machine Direction) % GB/T 15585 0.3
    Mold shrinkage(Transverse Direction) % GB/T 15585 0.6
    Water absorption (23°C-sat) % ISO 62 0.02

  • Mechanical properties
  •  
  •  
  •  
  • Tensile strength MPa ISO 527 145
    Elongation at Break (at Break) % ISO 527 1.2
    Flexural Modulus GPa ISO 178 19
    Flexural Strength MPa ISO178 240
    Charpy Impact Strength(V-notched) kJ/m² IS0 179 8

  • Thermal properties
  •  
  •  
  •  
  • Melting temperature (10°C/min) °C ISO 11357 280
    Heat Deflection Tem p High Load(1.8MPa) °C ISO 75 260
    Flammability class UL-94 V-0

  • Electrical properties
  •  
  •  
  •  
  • Dielectric Strength KV/mm IEC 60243 14
    Dielectric Constant
    IEC 60250 5
    Dissipation Factor
    IEC 60250 0.001
    Volume resistivity Ω•cm IEC 60093 1.6×1015
    CTI V IEC 60112 180

  • Test specimen production
  •  
  •  
  •  
  • Drying

    150℃&3h
    Injection Pressure MPa
    30~100
    Injection molding melt temperature °C ISO 294 290℃~330℃
    Injection molding mold temperature °C ISO 294 120℃~160℃
    Limit in-cylinder retention time

    300℃/60min
     320℃/30min