PPS-SGM601E65

Glass Fiber&Mineral Compounds PPS

PPS-SGM601E65 PPS is a 60% glass fiber and mineral reinforced linear polyphenylene sulfide compound developed to provide high modulus, low warp, excellent mechanical and electrical performance.

  • Property
  • Unit
  • Test Standard
  • Value
  • Physical properties
  •  
  •  
  •  
    • Density kg/m³ ISO 1183 1900
    Mold shrinkage(Machine Direction) % GB/T 15585 0.3
    Mold shrinkage(Transverse Direction) % GB/T 15585 0.6
    Water absorption (23°C-sat) % ISO 62 0.02

  • Mechanical properties
  •  
  •  
  •  
    • Tensile strength MPa ISO 527 155
    Elongation at Break (at Break) % ISO 527 1.2
    Flexural Modulus GPa ISO 178 19
    Flexural Strength MPa ISO178 245
    Charpy Impact Strength（V-notched） kJ/m² IS0 179 9

  • Thermal properties
  •  
  •  
  •  
    • Melting temperature (10°C/min) °C ISO 11357 280
    Heat Deflection Tem p High Load（1.8MPa） °C ISO 75 260
    Flammability class UL-94 V-0

  • Electrical properties
  •  
  •  
  •  
    • Dielectric Strength KV/mm IEC 60243 14
    Dielectric Constant
    		IEC 60250 5
    Dissipation Factor
    		IEC 60250 0.001
    Volume resistivity Ω•cm IEC 60093 1.6×1015
    CTI V IEC 60112 180

  • Test specimen production
  •  
  •  
  •  
    • Drying

    		150℃&3h
    Injection Pressure MPa
    		30~100
    Injection molding melt temperature °C ISO 294 290℃~330℃
    Injection molding mold temperature °C ISO 294 120℃~160℃
    Limit in-cylinder retention time

    300℃/60min

    320℃/30min