AS-SG401T87

Special purpose PPS

AS-SG401T87 is a glass fiber reinforced by PPS bassed PA66 aloy to provide excellent mechanical strength,toughness,and rigidity,along with excellent flow in thin-walled parts,low flash characteristics,and fast cycle times.It may be easily molded in conventional injection molding equipment utilizing water heated molds

  • Property
  • Unit
  • Test Standard
  • Value
  • Physical properties
  •  
  •  
  •  
  • Density kg/m³ ISO 1183 1550
    Mold shrinkage(Machine Direction) % GB/T 15585 0.3
    Mold shrinkage(Transverse Direction) % GB/T 15585 0.8
    Water absorption (23°C-sat) % ISO 62 0.2

  • Mechanical properties
  •  
  •  
  •  
  • Tensile strength MPa ISO 527 190
    Elongation at Break (at Break) % ISO 527 2
    Flexural Modulus GPa ISO 178 12
    Flexural Strength MPa ISO178 270
    Charpy Impact Strength(V-notched) kJ/m² IS0 179 10

  • Thermal properties
  •  
  •  
  •  
  • Melting temperature (10°C/min) °C ISO 11357 280
    Heat Deflection Tem p High Load(1.8MPa) °C ISO 75 250
    Flammability class UL-94 HB

  • Electrical properties
  •  
  •  
  •  
  • Dielectric Strength KV/mm IEC 60243 22
    Dielectric Constant
    IEC 60250 4
    Dissipation Factor
    IEC 60250 0.003
    Volume resistivity Ω•cm IEC 60093 1×1015
    CTI V IEC 60112 270

  • Test specimen production
  •  
  •  
  •  
  • Drying

    150℃&3h
    Injection Pressure MPa
    30~100
    Injection molding melt temperature °C ISO 294 290℃~330℃
    Injection molding mold temperature °C ISO 294 120℃~160℃
    Limit in-cylinder retention time

    300℃/60min

    320℃/30min